Novel high molecular weight diimide diacids and modified thermoplastic copolyether ester elastomers prepared therefrom

ABSTRACT

Novel diimide diacids and modified polyetherimide esters are prepared therefrom by reacting diols, dicarboxylic acids and a combination of the novel diimide diacid and dimer acid. These compositions have many excellent properties which make them particularly useful for extrusion and molding applications.

This application is a continuation of U.S. patent application Ser. No. 740,661, filed June 3, 1985, now U.S. Pat. No. 4,594,377, which is a division of U.S. patent application Ser. No. 665,315, filed Oct. 26, 1984, now U.S. Pat. No. 4,544,734.

The present invention relates to high molecular weight diimide diacids and esters thereof prepared from a polyoxyalkylene diamine and a tricarboxylic anhydride compound as defined herein.

The present invention also relates to novel, modified thermoplastic copolyetherimide ester elastomers having a high melting point with an improved crystallization rate and increased flexibility as well as improved solvent resistance than unmodified compositions.

Polyetherester imides are well known having been described in numerous publications and patents including for example, Honore et al, "Synthesis and Study of Various Reactive Oligmers and of Poly(ester-imide-ether)s, European Polymer Journal Vol. 16, pp. 909-916, Oct. 12, 1979; and in Kluiber et al, U.S. Pat. No. 3,274,159 and Wolfe Jr., U.S. Pat. Nos. 4,371,692 and 4,371,693, respectively. Additionally, McCready, U.S. Pat. No. 4,556,705 described a novel class of polyetherimide esters having a broad spectrum of superior physical properties including high melting point, excellent flexibility and/or excellent strain/stress characteristics.

While the foregoing polyetherimide ester elastomers have excellent physical properties, they are more susceptible to thermal and oxidative degradation as well as attack by solvents as a consequence of the presence of high amounts of various high molecular weight polyethers in the copolymer. However, the presence of the high molecular weight polyether is vital in order to manifest the physical properties, particularly the low flexural modulus, of such elastomeric compositions.

It is an object of the present invention to provide copolyetherimide esters which have improved thermal and oxidative stability without a loss in other physical properties.

It is also an object of the present invention to provide copolyetherimide esters having improved solvent resistance without sacrificing the superior flexibility of the polyetherimide ester.

Finally, it is an object of the present invention to provide copolyetherimide esters having a high melting point and improved crystallization rates combined with excellent flexibility.

It is has now been found that novel high molecular weight diimide diacids and diimide diesters having the foregoing qualities may be prepared from polyoxy alkylene diamines and a tricarboxylic component containing two imide forming vicinal carboxyl groups or an anhydride group and an additional carboxyl group. These diimide diesters and diimide diacids may be prepared in accordance with known methods for the preparation of diimides from diamines and anhydrides.

It has also been discovered that the foregoing diimide diacids may be used in the preparation of novel modified copolyetherimide esters having improved thermal and oxidative stability, solvent resistance and crystallization and flexibility characteristics. These can be prepared by conventional processes from (a) one or more diols, (b) one or more dicarboxylic acids and (c) a combination of (i) one or more polyoxyalkylene diimide diacides and (ii) one or more dimer acids, wherein the dimer acid is present in an amount of from about 5 to about 40 weight percent based on the combined weight of (i) and (ii). Preferred compositions encompassed by the present invention may be prepared from (a) one or more C₂ -C₁₅ aliphatic and/or cycloaliphatic diols, (b) one or more C₄ -C₁₆ aliphatic, cycloaliphatic and/or aromatic dicarboxylic acids or ester derivatives thereof and (c) a combination of (i) a polyoxyalkylene diimide diacid and (ii) a dimer acid wherein the dimer acid is present in an amount of from about 15 to about 30 weight percent based on the combined weight of (i) and (ii). The specific amounts of (i) polyoxyalkylene diimide diacid and (ii) dimer acid employed in the practice of the present invention is generally dependent upon the desired properties of the resultant polyetherimide ester. In general, the weight ratio of (c) the combination of (i) polyoxyalkylene diimide diacid and (ii) dimer acid to dicarboxylic acid (b) is from about 0.25 to 2.0, preferably from about 0.4 to about 1.4. Finally, the compositions may contain and preferably do contain additional stabilizers for even greater stabilization and low temperature impact strength.

Suitable diols (a) for use in preparing the compositions of the present invention include saturated and unsaturated aliphatic and cycloaliphatic dihydroxy compounds as well as aromatic dihydroxy compounds. These diols are preferably of a low molecular weight, i.e. having a molecular weight of about 250 or less. When used herein, the term "diols" and "low molecular weight diols" should be construed to include equivalent ester forming derivatives thereof, provided, however, that the molecular weight requirement pertains to the diol only and not to its derivatives. Exemplary of ester forming derivatives there may be given the acetates of the diols as well as for example ethylene oxide or ethylene carbonate for ethylene glycol.

Preferred saturated and unsaturated aliphatic and cycloaliphatic diols are those having from about 2 to 15 carbon atoms. Exemplary of these diols there may be given ethylene glycol, propanediol, butanediol, pentanediol, 2-methyl propanediol, 2,2-dimethyl propanediol, hexanediol, decanediol, 1,2-, 1,3- and 1,4- dihydroxy cyclohexane; 1,2-, 1,3- and 1,4-cyclohexane dimethanol; butene diol; hexene diol, etc. Especially preferred are 1,4-butanediol and mixtures thereof with hexanediol or butenediol, most preferably 1,4-butanediol.

Aromatic diols suitable for use in the practice of the present invention are generally those having from 6 to about 15 carbon atoms. Included among the aromatic dihydroxy compounds are resorcinol; hydroquinone; 1,5-dihydroxy naphthalene; 4,4'-dihydroxy diphenyl; bis(p-hydroxy phenyl)methane and bis(p-hydroxy phenyl) 2,2-propane.

Especially preferred diols are the saturated aliphatic diols, mixtures thereof and mixtures of a saturated diol(s) with an unsaturated diol(s), wherein each diol contains from 2 to about 8 carbon atoms. Where more than one diol is employed, it is preferred that at least about 60 mole %, based on the total diol content, be the same diol, most preferably at least 80 mole %. As mentioned above, the preferred compositions are those in which 1,4- butanediol is present in a predominant amount, most preferably when 1,4-butanediol is the only diol.

Dicarboxylic acids (b) which are suitable for use in the practice of the present invention are aliphatic, cycloaliphatic, and/or aromatic dicarboxylic acids. These acids are preferably of a low molecular weight, i.e., having a molecular weight of less than about 300. The term "dicarboxylic acids" as used herein, includes equivalents of dicarboxylic acids having two functional carboxyl groups which perform substantially like dicarboxylic acids in reaction with glycols and diols in forming polyester polymers. These equivalents include esters and ester-forming derivatives, such as acid halides and anhydrides. The molecular weight preference, mentioned above, pertains to the acid and not to its equivalent ester or ester-forming derivative. Thus, an ester of a dicarboxylic acid having a molecular weight greater than 300 or an acid equivalent of a dicarboxylic acid having a molecular weight greater than 300 are included provided the acid has a molecular weight below about 300. Additionally, the dicarboxylic acids may contain any substituent group(s) or combinations which do not substantially interfere with the polymer formation and use of the polymer of this invention.

Aliphatic dicarboxylic acids, as the term is used herein, refers to carboxylic acids having two carboxyl groups each of which is attached to a saturated carbon atom. If the carbon atom to which the carboxyl group is attached is saturated and is in a ring, the acid is cycloaliphatic.

Aromatic dicarboxylic acids, as the term is used herein, are dicarboxylic acids having two carboxyl groups each of which is attached to a carbon atom in an isolated or fused benzene ring system. It is not necessary that both functional carboxyl groups be attached to the same aromatic ring and where more than one ring is present, they can be joined by aliphatic or aromatic divalent radicals or divalent radicals such as -O--or --SO₂ --.

Representative aliphatic and cycloaliphatic acids which can be used for this invention are sebacic acid, 1,2-cyclohexane dicarboxylic acid, 1,3-cyclohexane dicarboxylic acid, 1,4-cyclohexane dicarboxylic acid, adipic acid, glutaric acid, succinic acid, oxalic acid, azelaic acid, diethylmalonic acid, allylmalonic acid, 4-cyclohexene-1,2- dicarboxylic acid, 2-ethylsuberic acid, tetramethylsuccinic acid, cyclopentanedicarboxylic acid, decahydro-1,5-naphthalene dicarboxylic acid, 4,4'- bicyclohexyl dicarboxylic acid, decahydro-2,6-naphthalene dicarboxylic acid, 4,4 methylenebis(cyclohexane carboxylic acid), and 1,1-cyclobutane dicarboxylic acid. Preferred aliphatic acids are cyclohexane dicarboxylic acids, sebacic acid, glutaric acid, azelaic acid and adipic acid.

Representative aromatic dicarboxylic acids which can be used include terephthalic, phthalic and isophthalic acids, bi-benzoic acid, substituted dicarboxy compounds with two benzene nuclei such as bis(p-carboxyphenyl) methane, oxybis(benzoic acid), ethylene-1,2-bis-(p-oxybenzoic acid), 1,5-naphthalene dicarboxylic acid, 3,4-furan dicarboxylic acid, 2,6-naphthalene dicarboxylic acid, 2,7-naphthalene dicarboxylic acid, phenanthrene dicarboxylic acid, anthracene dicarboxylic acid, 4,4'-sulfonyl dibenzoic acid, and halo and C₁ -C₁₂ alkyl, alkoxy, and aryl ring substitution derivatives thereof. Hydroxy acids such as p(B-hydroxyethoxy)-benzoic acid can also be used provided an aromatic dicarboxylic acid is also present.

Preferred dicarboxylic acids for the preparation of the polyetherimide esters of the present invention are the aromatic dicarboxylic acids, mixtures thereof and mixtures of one or more dicarboxylic acid with an aliphatic and/or cycloaliphatic dicarboxylic acid, most preferably the aromatic dicarboxylic acids. Among the aromatic acids, those with 8-16 carbon atoms are preferred, particularly the benzene dicarboxylic acids, i.e., phthalic, terephthalic and isophthalic acids and their dimethyl derivatives. Especially preferred is dimethyl terephthalate.

Finally, where mixtures of dicarboxylic acids are employed in the practice of the present invention, it is preferred that at least about 60 mole %, preferably at least about 80 mole %, based on 100 mole % of dicarboxylic acid (b) be of the same dicarboxylic acid or ester derivative thereof. As mentioned above, the preferred compositions are those in which dimethylterephthalate is the predominant dicarboxylic acid, most preferably when dimethylterephthalate is the only dicarboxylic acid.

The third component to be used in the practice of the present invention is a combination (c) of (i) polyoxyalkylene diimide diacid and (ii) dimer acid wherein the amount of dimer acid present is from about 5 to about 40 weight percent, preferably from about 15 to about 30 weight percent, based on the combined weight of (i) and (ii).

Polyoxyalkylene diimide diacids (i) suitable for use herein are high molecular weight diimide diacids wherein the number average molecular weight is greater than about 700, most preferably greater than about 900. They may be prepared by the imidization reaction of one or more tricarboxylic acid compounds containing two vicinal carboxyl groups or an anhydride group and an additional carboxyl group which must be esterifiable and preferably is nonimidizable with a high molecular weight polyoxyalkylene diamine.

These diimide diesters and diimide diacids may be prepared in accordance with known methods for the preparation of diimides from diamines and anhydrides.

The polyoxylalkylene diamines suitable for use in the present invention may be characterized by the following formula:

    H.sub.2 N--G--NH.sub.2                                     I

wherein G is the radical remaining after the removal of the amino groups of a long chain ether diamine. These polyether diprimary diamines are available commercially from Texaco Chemical Company under the trademark Jeffamine. In general they are prepared by known processes for the aminization of glycols. For example, they may be prepared by aminating the glycol in the presence of ammonia, Raney nickel catalyst and hydrogen as set forth in Belgium U.S. Pat. No. 634,741. Alternatively, they may be prepared by treating the glycol with ammonia and hydrogen over a Nickel-Copper-Chromium catalyst as taught by U.S. Pat. No. 3,654,370. Other methods for the production thereof include as taught in U.S. Pat. Nos. 3,155,728 and 3,236,895 and French Pat. Nos. 1,551,605 and 1,466,708. All the foregoing patents herein incorporated by reference.

The long chain ether glycols suitable for use in the manufacture of the polyoxyalkylene diamines are polymeric glycols having terminal (or as nearly terminal as possible) hydroxy groups and a number average molecular weight of from about 600 to about 12000. Additionally, the long chain ether glycols will have a carbon to oxygen ratio of from about 1.8:1 to about 4.3:1.

Representative long chain ether glycols are poly(ethylene ether)glycol; poly(propylene ether)glycol; poly(tetramethylene ether)glycol; random or block copolymers of ethylene oxide and propylene oxide, including propylene oxide terminated poly(ethylene ether) glycol; and random or block copolymers of tetrahydrofuran with minor amounts of a second monomer such as methyl tetrahydrofuran (used in proportion such that the carbon-to-oxygen mole ratio in the glycol does not exceed about 4.3). Especially preferred poly(alkylene ether)glycols are poly(propylene ether) glycol and poly(ethylene ether)glycols end capped with poly(propylene ether)glycol and/or propylene oxide.

In general, the polyoxyalkylene diamines useful within the scope of the present invention will have a number average molecular of from about 600 to 12000, preferably from about 900 to about 4000.

The tricarboxylic component may be almost any carboxylic acid anhydride containing an additional carboxylic group or the corresponding acid thereof containing two imide-forming vicinal carboxyl groups in lieu of the anhydride group. Mixtures thereof are also suitable. The additional carboxylic group must be esterifiable and preferably is substantially nonimidizable.

Further, while trimellitic anhdyride is preferred as the tricarboxylic component, any of a number of suitable tricarboxylic acid constituents will occur to those skilled in the art including 2,6,7 naphthalene tricarboxylic anhydride; 3,3',4 diphenyl tricarboxylic anhydride; 3,3',4 benzophenone tricarboxylic anhydride; 1,3,4 cyclopentane tricarboxylic anhydride; 2,2',3 diphenyl tricarboxylic anhydride; diphenyl sulfone -3,3',4 tricarboxylic anhydride, ethylene tricarboxylic anhydride; 1,2,5 naphthalene tricarboxylic anhydride; 1,2,4 butane tricarboxylic anhydride; diphenyl isopropylidene - 3,3',4 tricarboxylic anhydride; 3,4 dicarboxyphenyl 3-carboxylphenyl ether anhydride; 1,3,4 cyclohexane tricarboxylic anhydride; etc. These tricarboxylic acid materials can be characterized by the following formula: ##STR1## where R is a trivalent organic radical, preferably a C₂ to C₂₀ aliphatic, aromatic, or cycloaliphatic trivalent organic radical and R' is preferably hydrogen or a monovalent organic radical preferably selected from the group consisting of C₁ to C₆ aliphatic and/or cycloaliphatic radicals and C₆ to C₁₂ aromatic radicals, e.g. benzyl; most preferably hydrogen.

The amount of tricarboxylic component to be used in the preparation of the diimide diacids of the present invention is preferably two molar equivalents based on the number of moles of diamines. Obviously, less than two molar equivalents would result in incomplete imidization of the diamine. It is also possible to use more than two molar equivalents to assure optimal imidization.

The diimide diacids and diimide diesters of the present invention may be prepared by any of the known methods for the imidization of anhydrides with diamines. Exemplary of the methods include melt synthesis wherein the anhydride and diamine are heated at between about 100° C.-300° C., preferably from about 150°-250° C., while drawing off water, for several hours to produce the diimide. Alternatively, they may be produced by heating in a solvent including, for example, dimethylformamide, diethylformamide, diethylacetamide, N-methylcaprolactam, or dimethylsulfoxide, among others known to those skilled in the art, or in an azeotropic mixture of said solvent with an additional inert solvent, e.g. xylene, and refluxed at between about 100°-300° C., preferably from about 150° C.-250° C., for several hours to form the diimide. The solvent is subsequently removed by distillation and the residual solvent removed by vacuum drying to leave the diimide diacid as a viscous oily substance.

The resultant diimide diacids or diimide diester, as appropriate, is an oily substance, the viscosity of which is dependent in part upon the temperature and he specific diamine used, having a low melting point (generally less than about 250° C.) and good molecular flexibility. They may be represented by the following formula ##STR2## wherein R, R' and G are all as defined above. In general the diimide diacids of the present invention are free flowing and have a molecular weight of greater than about 700, preferably greater than about 900.

Dimer acids (ii) useful in the preparation of the copolyetherimide esters of the present invention are themselves prepared by the dimerization of unsaturated fatty acids of 18 carbons. Exemplary of fatty acids from which they are prepared there may be given oleic acid, linoleic acid and linolenic acid. The preparation and structure of dimer acid is described in Journal of the American Oil Chemists Society, 39, 534-545 (1962), Journal of the American Chemical Society 66, 84 (1944) and U.S. Pat. No. 2,347,562, all incorporated herein by reference. Suitable dimer acid may be employed in its unhydrogenated or hydrogenated form and include the sacid functioning derivatives thereof.

Several grades of dimer acid are available commercially which vary in monomer and trimer content. Inclusive of suitable commercial dimer acids there may be given those available from Emery Industries under the tradenames EMPOL 1010 (a hydrogenated dimer acid) and EMPOL 1014. EMPOL 1010 is reported as typically containing 97% dimer acid, 3% trimer acid and essentially no monobasic acid and extremely low unsaturation, whereas EMPOL 1014 is typified as containing 95%, 4% and 1% of dimer, trimer and monobasic acids respectively. Also available are the dimer acids sold under the tradename HYSTRENE from the Humko Products Division of Witco Chemical Corporation, especially HYSTRENE 3695 which typically contain 95% dimer acid and a weight ratio of dimer to trimer of 36:1. Preferred grades are substantially free of such monomer and trimer fractions, most preferably less than 5% by weight, and are fully saturated, or substantially so.

Where desirable, the dimer acid member may be substantially freed of monomer and trimer fractions by molecular distillation or other suitable means. In general, the dimer acid exists in the copolyetherimide ester as a soft or rubbery segment and accordingly dimer acids of relatively high molecular weight (preferably greater than about 500) are preferred so that the copolyetherimide esters are resilient, but do not deform until relatively high temperatures are reached.

Applicant has now found that novel copolyetherimide esters may be prepared having high melting temperatures, faster crystallization rates and greater flexibility than unmodified copolyetherimide esters by incorporating therein dimer acid. Specifically, applicants have found that copolyetherimide esters having comparable levels of polyoxyalkylene diimide diacid incorporated therein have less flexibility, resilience and impact properties, including, for example, low temperature impact. Alternatively, unmodified composition having essentially the same flexibility properties, resilience and so forth suffer from greater susceptability to oxidative and thermal degradation as well as manifest poorer solvent resistance, as a consequence of the higher levels of polyether component in the polymer. Thus by the practice of applicant's inventions one is able to achieve compositions of greater flexibility, crystalization rate solvent resistance and thermal and oxidative stability.

In general, the benefits of the present invention can be achieved by incorporating into the copolyetherimide ester from about 5 to about 40 weight percent, preferably from about 15 to about 30 weight percent, based on the combined weight of dimer acid and polyoxyalkylene diimide diacid of dimer acid.

Although the weight ratio of the above ingredients is not critical, it is preferred that the diol be present in at least a molar equivalent amount, preferably a molar excess, most preferably at least 150 mole based on the moles of dicarboxylic acid (b) and the combination (c) of (i) polyoxyalkylene diimide diacid and (ii) dimer acid, combined. Such molar excess of diol will allow for optimal yields, based on the amount of acids, while accounting for the loss of diol during esterification/condensation.

Further, while the amount by which the combination(s) of (i) polyoxyalkylene diimide diacid and (ii) dimer acid incorporated into the polymer is not critical to make the novel copolyetherimide esters of the present invention, it is preferred that the combination (c) be present in weight ratio to dicarboxylic acid (b) of from about 0.25:1 to about 2:1 preferably from about 0.4:1 to about 1.4:1 The actual weight ratio employed will be dependent upon the amount of dimer acid used, the specific polyoxyalkylene diimide diacid used and more importantly, the desired physical and chemical properties of the resultant polyetherimide ester. In general, the lower the ratio of the combination (c) of (i) polyoxyalkene diimide diacid (ii) and dimer acid to dicarboxylic acid the better the strength, crystallization and heat distortion properties of the polymer. Alternatively, the higher the ratio, the better the flexibility, tensile set and low temperature impact characteristics.

In its preferred embodiments, the compositions of the present invention will comprise the reaction product of dimethylterephthalate, optionally with up to 40 mole % of another dicarboxylic acid; 1,4-butanediol, optionally with up to 40 mole % of another saturated or unsaturated aliphatic and/or cycloaliphatic diol; and a combination of (i) a polyoxyalkylene diimide diacid prepared from a polyoxyalkylene diamine of molecular weight of from about 600 to about 12000, preferably from about 900 to about 4000 and (ii) dimer acid in an amount of from about 10 to about 40% by weight, most preferably from about 15 to about 30% by weight based on the combined weight of (i) and (ii), and optionally trimellitic anhydride. In its most preferred embodiments, the diol will be 100 mole % 1,4butanediol and the dicarboxylic acid 100 mole % dimethylterephthalate.

The novel polyetherimide esters described herein may be prepared by conventional esterification/condensation reactions for the production of polyesters. Exemplary of the processes that may be practiced are as set forth in, for example, U.S. Pat. Nos. 3,023,192; 3,763,109; 3,651,014; 3,663,653 and 3,801,547, herein incorporated by reference. Additionally, these compositions may be prepared by such processes and other known processes to effect random copolymers, block copolymers or hybrids thereof wherein both random and block units are present.

It is customary and preferred to utilize a catalyst in the process for the production of the polyetherimide esters of the present invention. In general, any of the known ester-interchange and polycondensation catalysts may be used. Although two separate catalysts or catalyst systems may be used, one for ester interchange and one for polycondensation, it is preferred, where appropriate, to use one catalyst or catalyst system for both. In those instances where two separate catalysts are used, it is preferred and advantageous to render the ester-interchange catalyst ineffective following the completion of the precondensation reaction by means of known catalyst inhibitors or quenchers, in particular, phosphorus compounds such as phosphoric acid, phosphenic acid, phosphonic acid and the alkyl or aryl esters or salts thereof, in order to increase the thermal stability of the resultant polymer.

Exemplary of the suitable known catalysts there may be given the acetates, carboxylates, hydroxides, oxides, alcoholates or organic complex compounds of zinc, manganese, antimony, cobalt, lead, calcium and the alkali metals insofar as these compounds are soluble in the reaction mixture. Specific examples include, zinc acetate, calcium acetate and combinations thereof with antimony tri-oxide and the like. These catalysts as well as additional useful catalysts are described in U.S. Pat. Nos. 2,465,319; 2,534,028; 2,850,483; 2,892,815; 2,937,160; 2,998,412; 3,047,539; 3,110,693 and 3,385,830, among others, incorporated herein by reference.

Where the reactants and reactions allow, it is preferred to use the titanium catalysts including the inorganic and organic titanium containing catalysts, such as those described in, for example, U.S. Pat. No. 2,720,502; 2,727,881; 2,729,619; 2,822 348; 2,906,737; 3,047,515; 3,056,817; 3,056,818; and 3,075,952 among others, incorporated herein by reference. Especially preferred are the organic titanates such as tetra-butyl titanate, tetra-isopropyl titanate and tetra-octyl titanate and the complex titanates derived from alkali or alkaline earth metal alkoxides and titanate esters, most preferably the organic titanates. These too may be used alone or in combination with other catalysts such as for example, zinc acetate, manganese acetate or antimony trioxide, and/or with a catalyst quencher as described above.

Although the novel polyetherimide ester of the present invention possess many desirable properties, including improved stability as compared to unmodified polymers, it may be preferred to further enhance stabilization of these compositions to heat, oxidation, radiation by UV light and the like. This can be accomplished by incorporating stabilizer materials into the compositions either during production or while in a hot melt stage following polymerization. The particular stabilizers useful herein are any of those known in the art which are suitable for polyetherimide esters.

Satisfactory stabilizers comprise phenols and their derivatives, amines and their derivatives, compounds containing both hydroxyl and amine groups, hydroxyazines, oximes, polymeric phenolic esters and salts of multivalent metals in which the metal is in its lower valence state.

Representative phenol derivatives useful as stabilizers include 3,5-di-tert-butyl-4-hydroxy hydrocinnamic triester with 1,3,5-tris-(2-hydroxyethyl)-s-triazine-2,4,6-(1H,3H,5H)trione; 4,4'-bis(2,6-ditertiary-butylphenol); 1,3,5-trimethyl-2,4,6-tris(3,5-ditertiary-butyl-4-hydroxybenzyl)benzene and 4,4'-butylidene-bis(6-tertiary-butyl-m-cresol). Various inorganic metal salts or hydroxides can be used as well as organic complexes such as nickel dibutyl dithiocarbonate, manganous salicylate and copper 3-phenyl-salicylate. Typical amine stabilizers include N,N'-bis(betanaphthyl)-p-phenylene diamine; N,N'-bis(1-methylheptyl)-p-phenylene diamine and either phenyl-beta-naphthyl amine or its reaction products with aldehydes. Mixtures of hindered phenols with esters of thiodipropionic acid, mercaptides and phosphite esters are particularly useful. Additional stabilization to ultraviolet light can be obtained by compounding with various UV absorbers such as substituted benzophenones and/or benzotriazoles.

Optionally, it may be desirable to add a minor amount, up to about 20 mole %, preferably up to about 10 mole %, based on the moles of the polyoxyalkylene diimide diacid, of a tricarboxylic component to the reaction mixture. While higher amounts of the tricarboxylic component may be used, this has the disadvantage of reducing some of the beneficial properties of the present polymers. Suitable tricarboxylic components are the same as identified above for the preparation of the polyoxyalkylene diimide diacid. While it is preferred that the additional tricarboxylic component be the same as used in the preparation of the polyoxyalkylene diimide diacid, it is not necessary. The addition of the tricarboxylic acid component will have the added benefit of picking up and reacting with any residual, unreacted amine groups and, consequently, aiding in the viscosity build of the polymer itself.

Further, the properties of these polyesters can be modified by incorporation of various conventional inorganic fillers such as carbon black, silica gel, alumina, clays and chopped fiberglass. These may be incorporated in amounts up to 50% by weight, preferably up to about 30% by weight. In general, these additives have the effect of increasing the modulus of the material at various elongations.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The following examples are presented as illustrative of the present invention and are not to be construed as limiting thereof.

Physical properties were determined according the proper ASTM methods as follows:

    ______________________________________                                         Flexural Modulus     ASTM D 790                                                Tensile Elongation   ASTM D 638                                                Shore D Hardness     ASTM D 2240                                               ______________________________________                                    

In general, all compositions were prepared by placing all reactants in the reaction vessel and heating to 180° C. After the theoretical amount of methanol was removed, the pot temperature was increased to about 250° C. and a vacuum applied (<1mm Hg) until the desired viscosity polymer was obtained. All reactions, unless otherwise specified were catalyzed with tetraoctyl titanate catalyst.

Diimide Diacid A

Into a reaction vessel were placed 100 parts by weight of Jeffamine® D2000 (amine terminated polyoxypropylene glycol--approx. MW 2000 from Texaco Chemical Company) and 19.2 parts by weight of trimellitic anhydride and an excess of an azeotropic solvent mixture of 80/20 dimethylformamide/xylene to solublize the foregoing. (Xylene was employed in order to observe the formation of water during the reaction.) The mixture was heated to and refluxed at the reflux temperature of the solvent mixture for about 3 hours. The solvent mixture was distilled off and the remaining diimide diacid vacuum dried to remove residual solvent leaving a viscous oily substance identified as the diimide diacid reaction product of the reactants.

Diimide Diacid B

Into a reaction vessel was placed 100 parts by weight of Jeffamine® ED900 (amine terminated poly-(ethylene oxide--propylene oxide)glycol approximate MW 900 - Texaco Chemical Company) and 42.7 parts by weight trimellitic anhydride. The mixture was heated and stirred at 180° C. for two hours during which time water was distilled off. The reaction produced a viscous oily diimide diacid.

Diimide Diacid C and D

Additional diimide diacids were prepared as in Example 2 utilizing Jeffamine® D2000 and Jeffamine ED2001 [amine terminated poly(propylene oxide)glycol-approx. MW 2000 and amine terminated poly(ethylene oxide--propylene oxide)glycol approx. MW 2000 having a predominately poly(ethylene oxide) backbone, respectively] and trimellitic anhydride in a mole ratio of 1:2 Jeffamine: TMA. These reactions also produced viscous oily diimide diacids.

EXAMPLES E1-E4, COMPARATIVE EXAMPLES CE1-CE6

A series of examples were prepared typifying the modified copolyetherimide esters of the present invention and unmodified copolyetherimide esters. In addition to demonstrating the benefits attributed to these compositions, these examples demonstrate the broad application of the present teaching giving examples with different amounts of dimer, varying weight ratio of (i) polyoxyalkylene diimide diacids and (ii) dimer to dicarboxylic acid (b) and various polyoxyalkylene diimide diacids. The specific compositions of each example and comparative example as well as the physical properties thereof are set forth in Table 1. All components are expressed in parts by weight unless otherwise stated.

                                      TABLE 1                                      __________________________________________________________________________                   E1  CE1 E2  CE2 E3  CE3 E4  CE4 CE5 CE6                          __________________________________________________________________________     1,4-Butanediol                                                                               30  32  32  36  31  32  32  33  30  30                           Dimethylterephthalate                                                                        36  40  38  46  37  40  38  42  38  38                           Hystrene 3695 Dimer                                                                          7   --  10.5                                                                               --  5   --  5   --  --  --                           Diimide Diacid A                                                                             --  --  --  --  27  28  25  25  32  --                           Diimide Diacid B                                                                             27  28  20  18  --  --  --  --  --  32                           Stabilizer.sup.a                                                                             --  3   --  3   --  3   5   3   3   3                            Trimelletic Anhydride.sup.b                                                                  --  3.2 --  3.2 --  7.2 --  7.3 7.4 3.3                          Properties                                                                     Melting Point, °C.                                                                    191 194 193 208 201 210 201 214 203 190                          Flexural Modulus, psi × 10.sup.3                                                       19.2                                                                               25  --  52  16.9                                                                               24  18  32  16  20                           Tensile Elongation                                                                           619 --  --  --  334 --  --  --  --  --                           Shore D Hardness                                                                             48  --  --  --  48  --  --  --  --  --                           __________________________________________________________________________      .sup.a phenol derived stabilizer, amt is % by wt. based on amount of           diimide diacids.                                                               .sup.b in mole % based on the number of moles of diimide diacid.         

From the examples in Table 1 it is clear that the compositions of the present invention have improved flexibility at the same or about the same levels of incorporation of polyoxyalkylene diimide diacid. For example comparison of Example E1, E3 and E4 with comparative Examples CE1, CE3 and CE4 respectively demonstrates the improved flexibility of the composition of the present invention.

Alternatively, unmodified compositions having about the same flexibility as the modified polyetherimide ester compositions of the present invention require about a 20% increase in the amount of polyoxyalkylene diimide diacid component. Because of the susceptability of the polyether component to thermal and oxidative degradation as well as attack by solvents, applicant's composition by virtue of lesser amounts of polyether will have enchanced thermal and oxidative stability as well as improved solvent resistance as compared to the unmodified compositions.

Obviously, other modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments of the invention described which are within the full intended scope as defined by the appended claims. 

I claim:
 1. The imidization reaction product of(a) a tricarboxylic acid anhydride or the corresponding acid thereof containing two vicinal carboxyl groups and (b) a polyoxyalkylene diamine of the formula

    H.sub.2 N--G--NH.sub.2

wherein G is the divalent radical remaining after the removal of the amino groups of a long chain poly(alkylene ether) diamine having a molecular weight of from about 600 to about 12000 and a carbon to oxygen, ratio of from about 1.8:1 to about 4.3:1.
 2. The reaction product of claim 1 wherein the tricarboxylic acid anhydride is represented by the formula: ##STR3## wherein R a C₂ to C₂₀ organic aliphatic, cycloaliphatic or aromatic trivalent radical having two vicinal reactive sites and R' is selected from the group consisting of hydrogen, or a monovalent organic radical selected from the group consisting of a C₁ to C₆ aliphatic or cycloaliphatic hydrocarbon radical or a C₆ to C₁₂ aromatic radical.
 3. The reaction product of claim 1 wherein the tricarboxylic acid anhydride is trimellitic anhydride.
 4. The reaction product of claim 1 wherein the polyoxyalkylene diamine is selected from the group consisting of poly(propylene ether) diamine, poly(tetramethylene ether) diamine and co-poly(ethylene ether-propylene ether) diamine.
 5. The reaction product of claim 1 wherein the polyoxyalkylene diamine is poly(propylene ether) diamine.
 6. The reaction product of claim 1 wherein the polyoxyalkylene diamine is co-poly-(ethylene ether-propylene ether) diamine have a predominately polyethylene ether backbone.
 7. High molecular weight poly ether diamide diacids of the formula: ##STR4## wherein each R is independently selected from the group consisting of C₂ to C₂₀ aliphatic and cycloaliphatic trivalent organic radicals and C₆ to C₂₀ aromatic trivalent organic radicals having two vicinal reactive sites; each R' is independently selected from the group consisting of hydrogen, C₁ to C₆ aliphatic and cycloaliphatic monovalent organic radicals and C₆ to C₁₂ aromatic monovalent organic radicals, and G is the radical remaining after removal of the amino groups of a long chain ether diamine having an average molecular weight of from about 600 to 12,000.
 8. The diimide diacid of claim 7 wherein R is a trivalent 6 membered aromatic hydrocarbon and R' is hydrogen.
 9. The diimide diacid of claim 7 wherein G is the divalent radical remaining after removal of the terminal amino groups of a long chain ether diamine having a molecular weight of from about 900 to about
 4000. 10. The diimide diacid of claim 7 wherein G is the divalent radical remaining after removal of the terminal amino groups of a long chain poly(alkylene ether) diamine selected from the group consisting of poly(ethylene ether) diamine, poly(tetramethylene ether) diamine, and a random or block copoly(ethylene ether-propylene ether) diamine.
 11. The diimide diacid of claim 7 wherein G is the divalent radical remaining after removal of the terminal amino groups of poly(propylene ether) diamine.
 12. The diimide diacid of claim 7 wherein G is the divalent radical remaining after removal of the terminal amino groups of a co-poly(propylene ether-ethylene ether) diamine.
 13. The diimide diacid of claim 12 wherein the co-poly(propylene ether-ethylene ether) diamine has a predominately poly(ethylene ether) backbone.
 14. The diimide diacid of claim 8 wherein R is the radical remaining after removal of the carboxylic group of trimellitic acid or trimellitic anhydride, respectively.
 15. The diimide diacid of claim 14, wherein R is derived from trimellitic anhydride. 